We are one of the leading Manufacturer , Supplier & Exporters of High quality API 5L X70 PSL 2 Pipes. We manufacture these Seamless Steel Pipes using extreme grade of raw material. These pipes are applicable in critical engineering applications where heat treatments are inaugurated. These pipes are used for special applications in different industries including oil and natural gas and also in different structural applications. We offer these in different dimensions, shapes, sizes, material specifications as per clients own requirement. We offer them at industry leading prices.
| Sizes (Seamless) | : | 1/2” NB - 60” NB |
| Sizes (ERW) | : | 1/2” NB - 24” NB |
| Sizes (SAW) | : | 16” NB - 100” NB |
| Sizes LSAW/DSAW | : | 16'OD TO 54' OD (8 MM TO 50 MM THK) |
| Wall Thickness | : | SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness |
| Dimensions | : | All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API. |
| Additional Testing | : | NACE MR0175, NACE TM0177, NACE TM0284, HIC TEST, SSC TEST, H2 SERVICE, IBR, etc. |
| Mass fraction, based upon heat and product analysis % maximum | CARBON EQUIVALENT a | ||||||||||
| % MAXIMUM | |||||||||||
| Cb | Si | Mnb | P | S | V | Nb | Ti | Other | CEIIW | CEPcm | |
| SEAMLESS & WELDED PIPES | |||||||||||
| L485Q or X70Q | 0.18f | 0.45f | 1.8f | 0.025 | 0.015 | g | g | g | h | 0.43 | 0.25 |
| WELDED PIPE | |||||||||||
| L485M OR X70M | 0.12f | 0.45f | 1.7f | 0.025 | 0.015 | g | g | g | h | 0.43f | 0.25 |
| Y.S | T.S | ELONGATION |
| Mpa(psi) | Mpa(psi) | |
| min | min | min |
| 485(70 300) | 635(92 100) | F |
| IMPACT TEST | |
| AVG. ABSORBED ENERGY | IND. ABSORBED ENERGY |
| Min.(joules) | Min.(joules) |
| 27 | 20 |
• Unless otherwise agreed, the sum of th niobium & vanadum concentrations shall be = 0.06%
• Unless otherwise agreed, 0.50% maximum for copper, 0.30% maximum for nickel, 0.30% maximum for chromium, & 0.15% maximum for molybdenum.
• The sum of th niobium & vanadum & titanium concentrations shall be =0.15%
• Unless otherwise agreed, 0.50% maximum for copper, 0.30% maximum for nickel, 0.30% maximum for chromium, & 0.15% maximum for molybdenum.
• Unless otherwise agreed g unless otheriwse agreed the sum of th niobium & vanadum & titanium concentrations shall be =0.15%